1£©High Temperature Burnt Slide Plate 

This product adopts tabular alumina, carbonaceous material and zirconia-containing material as main raw materials, adds in high performance antioxidants, uses phenolic resin as binder, formed under high-pressure and burned under high temperature. The slide plates have the advantages of high strength, good erosion resistance, thermal shock resistance and good stability etc., mainly used in large and medium-sized ladle.

The physical and chemical properties of high temperature burned Al-C and Al-Zr-C slide plate are as follow:

Chemical and Physical Properties

Al-C Slide Gate Plate

Al-Zr-C Slide Gate Plate

LQSP-70

LQSP -75

LQSP -80

LQSP -85

LQSP -86

LQSP -70

LQHSP-75

LQHSP -77

Al2O3,%

70

75

80

85

86

70

75

77

C,%

7

7

5

5

4

7

7

7

ZrO2,%

-

-

-

-

-

6

6

2.5

A.P.,%   max

10

10

10

10

7

10

10

10

B.D.,g/cm3

2.8

2.9

2.9

3.0

2.95

3.00

3.05

2.90

C.C.S.,   MPa  min

65

70

100

100

100

110

115

100

 

2£© Low Temperature Burnt Slide Plate

Tabular alumina, zirconia-containing material and spinel as major raw materials, adding in special metal, using phenolic resin as binder, being burned under low temperature to produce the products, which have the advantages of low carbon content, strong strength under high temperature and good thermal shock resistance stability. This product mainly used in small and medium-sized, ladle.

 

Chemical and Physical Properties

Low Temperature Burnt Slide Gate Plate

LQLTSP-70

LQLTSP-75

LQLTSP-80

LQLTSP-85

LQLTSP-86

Al2O3,%  min

70

75

80

85

86

C,%

¡Ý5

¡Ý5

¡Ý5

¡Ý4

4

A.P.,%  max

10

10

10

8

7

B.D.,g/cm

2.9

2.95

3.00

3.10

2.95

C.C.S.,

MPa ¡Ý

90

90

100

120

100

3£© Unburned Slide Plate

To meet the needs of continuous casting and reducing steelmaking costs for small and medium-sized steel plant, we have developed unburned slide gate series products¡ªunburned Al-C slide plate, which adopts tabular alumina and high pure graphite, adds in proper amount of additive and antioxidant, uses phenolic resin as binder, pressed under press machine. The unburned Al-C plates have the following features: no need to be burned, tar impregnated and distilled, simple processing. This product mainly used in small and medium-sized ladle.

The physical and chemical properties of unburned Al-C slide plate are as follow:

Chemical and Physical Properties

Al-C Slide Gate Plate

LQUSP-70

LQUSP-75

LQUSP-80

LQUSP-85

LQUSP-86

Al2O3,%  

70

75

80

85

86

C,%

7

7

5

5

4

A.P.,%  max

10

10

8

10

7

B.D. g/cm  min

2.8

2.9

3.0

3.0

2.95

C.C.S., MPa  min

65

70

100

100

100

     
 


Products Center

 
 
Contact us

Sales: Alice
Tel: +86-531-87061168
Fax: +86-531-87061162
Email/msn:
¡¡¡¡alice@lqtrade.com
¡¡¡¡refractory@lqtrade.com

 
Copyright 2008 Linquan Refractory Company All Right Reserved.
³ICP±¸09102045ºÅ